پلی متیل متاکریلات
Chi Mei - Taiwan PMMA |
SORT |
PMMA |
||
Name |
CM-205 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
General |
Melt Index |
D1238 |
230°C, 3.8 Kg |
g/10min |
1.8 |
Mass Density |
D792 |
23°C |
- |
1.19 |
Bulk Density |
D1182 |
- |
gr/cm^3 |
0.7 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.3 |
Molding Shrinkage(1/8') |
D955 |
- |
% |
0.2~0.6 |
Hardness |
D785 |
M-scale |
- |
95 |
Refractive Index |
D542 |
- |
- |
1.491 |
Light Transmission |
D1003 |
- |
% |
92 |
Tensile Strength (Break) |
D638 |
6mm/min |
Kg/cm^2 |
750 |
lb/in^2 |
10600 |
|||
Tensile Elongation |
D638 |
6mm/min |
% |
10 |
Flexural Strength |
D790 |
2.8mm/min |
Kg/cm^2 |
1200 |
lb/in^2 |
17000 |
|||
Izod Impact Strength |
D256 |
6.4mm, 23°C |
Kg.cm/cm |
2 |
ft.lb/in |
0.37 |
|||
Flammability |
UL94 |
1.5 mm |
- |
HB |
Heat Deflection Temperature |
D648 |
Unannealled |
°F |
216 |
°C |
102 |
|||
Vicat Softening Temperature |
D1525 |
1 Kg, 50°C/hr |
°F |
239 |
°C |
115 |